Handle Tech Specs
HANDLE-TECH SPECS AND CONSTRUCTION MATERIAL INFORMATION
Handle-Tech is a tool that makes picking up and carrying industrial pipes and hoses easier and safer. Use Handle-Tech to help reduce injuries, stay clean and speed up your work.
All our standard Handle-Tech handles are composed of Long Glass Nylon which enhances the thermal properties compared to commonly used materials such as aluminum; in addition, this lightweight material is stronger and more wear-resistant. From temperatures of -40C to +50C, each handle is designed to battle the most hostile environments. The Handle-Tech Handle has a safe lifting capacity of 400 lbs with a breaking point at 1125 lbs. PLEASE NOTE that this device was designed for hand-use only and should only be used as designed. The following specifications apply to all Handle-Tech handles:
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 88.0 - 100 | 88.0 - 100 | Average value: 94.0 Grade Count:4 |
| Hardness, Rockwell R | 115 - 122 | 115 - 122 | Average value: 120 Grade Count:16 |
| Tensile Strength, Ultimate | 165 - 318 MPa | 23900 - 46100 psi | Average value: 237 MPa Grade Count:21 |
| Tensile Strength, Ultimate | 127 - 353.701 MPa, @Temperature -40.0 - 121 °C | 18400 - 51300.1 psi, @Temperature -40.0 - 250 °F | Average value: 147 MPa Grade Count:3 |
| Tensile Strength, Ultimate | 95.0 - 130 MPa @Temperature 130 - 175 °C | 13800 - 18900 psi @Temperature 266 - 347 °F | Average value: 147 MPa Grade Count:2 |
| Tensile Strength, Ultimate | 95.0 - 130 MPa @Time 1.80e+7 - 7.20e+7 sec | 13800 - 18900 psi @Time 5000 - 20000 hour | Average value: 147 MPa Grade Count:2 |
| Tensile Strength, Yield | 148 - 285 MPa | 21500 - 41300 psi | Average value: 223 MPa Grade Count:21 |
| Tensile Strength, Yield | 144.79 - 144.79 MPa @Temperature 93.3 - 93.3 °C | 21000 - 21000 psi @Temperature 200 - 200 °F | Average value: 145 MPa Grade Count:1 |
| Elongation at Break | 1.20 - 4.00 % | 1.20 - 4.00 % | Average value: 1.99 % Grade Count:37 |
| Elongation at Break | 1.80 - 2.20 % @Temperature -40.0 - 121 °C | 1.80 - 2.20 % @Temperature -40.0 - 250 °F | Average value: 1.98 % Grade Count:2 |
| Modulus of Elasticity | 10.3 - 23.2 GPa | 1500 - 3360 ksi | Average value: 18.9 GPa Grade Count:20 |
| Modulus of Elasticity | 11.9 - 20.8566 GPa @Temperature -40.0 - 121 °C | 1730 - 3025.05 ksi @Temperature -40.0 - 250 °F | Average value: 14.9 GPa Grade Count:2 |
| Flexural Yield Strength | 234 - 460 MPa | 33900 - 66700 psi | Average value: 350 MPa Grade Count:39 |
| Flexural Yield Strength | 260 - 260 MPa @Temperature 80.0 - 80.0 °C | 37700 - 37700 psi @Temperature 176 - 176 °F | Average value: 260 MPa Grade Count:1 |
| Flexural Modulus | 0.461 - 22.8 GPa | 66.9 - 3300 ksi | Average value: 17.4 GPa Grade Count:39 |
| Flexural Modulus | 0.227527 - 19.3053 GPa @Temperature -40.0 - 121 °C | 33.0005 - 2800.04 ksi @Temperature -40.0 - 250 °F | Average value: 9.78 GPa Grade Count:4 |
| Izod Impact, Notched | 0.950 - 6.62 J/cm | 1.78 - 12.4 ft-lb/in | Average value: 2.27 J/cm Grade Count:33 |
| Izod Impact, Notched | 1.30 - 7.68816 J/cm @Temperature -40.0 - 149 °C | 2.44 - 14.4031 ft-lb/in @Temperature -40.0 - 300 °F | Average value: 4.51 J/cm Grade Count:2 |
| Izod Impact, Unnotched | 10.7 - 5340 J/cm | 20.0 - 10000 ft-lb/in | Average value: 26.4 J/cm Grade Count:16 |
| Izod Impact, Notched (ISO) | 11.0 - 30.0 kJ/m² | 5.23 - 14.3 ft-lb/in² | Average value: 15.8 kJ/m² Grade Count:3 |
| Charpy Impact Unnotched | 6.50 - 15.0 J/cm² | 30.9 - 71.4 ft-lb/in² | Average value: 10.0 J/cm² Grade Count:9 |
| 6.00 - 9.70 J/cm² @Temperature -40.0 - 30.0 °C | 28.6 - 46.2 ft-lb/in² @Temperature -40.0 - 86.0 °F | Average value: 8.05 J/cm² Grade Count:7 | |
| Charpy Impact, Notched | 1.30 - 5.40 J/cm² | 6.19 - 25.7 ft-lb/in² | Average value: 2.68 J/cm² Grade Count:9 |
| Charpy Impact, Notched | 1.20 - 4.60 J/cm² @Temperature -30.0 - 30.0 °C | 5.71 - 21.9 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 1.88 J/cm² Grade Count:6 |
| Dart Drop, Total Energy | 7.85 - 16.4 J @Temperature -20.0 - -20.0 °C | 5.79 - 12.1 ft-lb @Temperature -4.00 - -4.00 °F | Average value: 12.1 J Grade Count:1 |
| Dart Drop, Total Energy | 7.85 - 16.4 J @Thickness 3.18 - 3.18 mm | 5.79 - 12.1 ft-lb @Thickness 0.125 - 0.125 in | Average value: 12.1 J Grade Count:1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+9 - 1.00e+16 ohm-cm | 1.00e+9 - 1.00e+16 ohm-cm | Average value: 6.94e+14 ohm-cm Grade Count:15 |
| Surface Resistance | 1.00e+10 - 1.00e+16 ohm | 1.00e+10 - 1.00e+16 ohm | Average value: 8.50e+14 ohm Grade Count:12 |
| Dielectric Strength | 19.7 - 22.0 kV/mm | 500 - 559 kV/in | Average value: 19.9 kV/mm Grade Count:14 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.0 - 27.0 µm/m-°C | 5.56 - 15.0 µin/in-°F | Average value: 21.5 µm/m-°C Grade Count:18 |
| Thermal Conductivity | 0.300 - 0.548 W/m-K | 2.08 - 3.80 BTU-in/hr-ft²-°F | Average value: 0.424 W/m-K Grade Count:4 |
| Melting Point | 220 - 262 °C | 428 - 504 °F | Average value: 253 °C Grade Count:11 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 - 262 °C | 428 - 504 °F | Average value: 254 °C Grade Count:11 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 - 263 °C | 410 - 505 °F | Average value: 251 °C Grade Count:37 |
| Flammability, UL94 | HB | HB | Grade Count:12 |